- Title
- Lean methane combustion over palladium loaded on alumina and HBETA zeolite: the role of the support on water vapour inhibition
- Creator
- Hosseiniamoli, Hadi; Kennedy, Eric M.; Stockenhuber, Michael
- Relation
- 11th Asia-Pacific Conference on Combustion (ASPACC 2017). Proceedings of the 11th Asia-Pacific Conference on Combustion (Sydney 10-14 December, 2017)
- Publisher
- UNSW
- Resource Type
- conference paper
- Date
- 2017
- Description
- Catalytic combustion of ventilation air methane is a potential solution for abatement of this greenhouse gas (GHG) source. A leading hypothesis for the observed catalyst deactivation of palladium-based catalysts when operating at low temperature is water poisoning. In this research, high silica BETA and alumina solids were used as supports for the Pd-based catalyst. The long term stability of methane conversion is significantly improved over HBETA compared to alumina supported Pd. TEM and chemisorption analyses confirms a greater level of dispersion of Pd in the HBETA compared to alumina support. TPD results shows that the Pd/Alumina catalyst adsorbs more water vapour at lower temperatures compared to Pd/HBETA resulting in an enhancement in the extent of water inhibition. Evidence for the presence of stored oxygen was observed in oxygen desorption results, where oxygen and water were co-adsorbed over the samples. This feature is also consistent with the supposition that Pd/HBETA has greater lattice oxygen mobility and a higher potential storage capacity compared to that of Pd/Al₂O₃. In addition, it was found that at lower temperatures, the effective surface coverage of oxygen was higher for Pd/HBETA compared to Pd/Alumina which was confirmed by TPD analysis.
- Subject
- catalyst deactivation; methane conversion; oxygen adsorption; aluminium; resources engineering; physical chemistry; industry
- Identifier
- http://hdl.handle.net/1959.13/1387705
- Identifier
- uon:32657
- Language
- eng
- Reviewed
- Hits: 1094
- Visitors: 1245
- Downloads: 0
Thumbnail | File | Description | Size | Format |
---|